Zhangjiagang Huachuang Engineering Plastics Co., Ltd
|Place of Origin:||China|
|Minimum Order Quantity:||1 ton|
|Packaging Details:||25 kg per bag|
|Delivery Time:||5-8 working days|
|Supply Ability:||20 tons per day|
|Applied:||Thermal Break Profiles||Glass Fiber Content:||25%|
|Fiber Type:||GFRP||Plastic Properties After Heated:||Thermoplastic Plastics|
PA66 is copolymerization for extrusion molding. PA66 is safe and reliable with excellent stability.
The product is based on PA66 resin. It is produced by twin-screw extruder after adding glass fiber and various additives.
Its characteristics are high mechanical strength, large modulus, good wear resistance, stable size and long-term work at high temperature.
Model NO.: PA66GF25
Material: Polyamide6.6 and glass fiber
Usage: General Plastics, Engineering Plastics, Specialty Plastics and Heat insulation plastics
Plastic Properties After Heated: Thermoplastic Plastics
Plastic Forming Method: Extrusion molding
Export Markets: Global
Bangyu PA66 Granules Performance Table
|NO.||Item||Unit||GB/T 23615.1-2009||BY-Technical specification|
|2||Linear expansion coefficient||K-1||(2.3-3.5)×10-5||(2.3-3.5)×10-5|
|3||Vicat softening temperature||ºC||≥230ºC||≥233ºC|
|5||Testing for tensile cracks||-||No cracks||No cracks|
|10||Elongation at break||%||≥2.5||≥2.6|
|12||High temperature tensile strength(transverse)||MPa||≥45a||≥47a|
|13||Low temperature tensile strength(transverse)||MPa||≥80a||≥81a|
|14||Water resistance tensile strength(transverse)||MPa||≥35a||≥35a|
|15||Aging resistance tensile strength(transverse)||MPa||≥50a||≥50a|
1.Sample water content less than 0.2% by weight.
2.Norm laboratory condition:(23±2)ºC and (50±10)% relative humidity.
3.The specifications marked with "a" only applies to I-shape strip otherwise, the specifications concluded between supplier and buyer through consultation, shall be written in contract or purchase order.
Packaging & Delivery info
Packaging details: 25kg/bag
Delivery details: shipped in 5-8 working days after receiving the payment
Please feel free to contact us if you have any questions.
Contact Person: Camille Cai